Preparation |
CEN 14780 |
|
total moisture |
CEN 14774-1 |
|
(inherent) moisture of analysis sample |
CEN 14774-3 |
|
Ash 550°C |
CEN 14775 |
|
Ash 815°C |
ISO 1171 |
|
volatile matter 900°C |
CEN 15148 |
|
total sulfur S |
CEN 15289 |
|
total carbon C (TC) |
CEN 15104 |
|
Nitrogen N |
CEN 15104 |
|
Hydrogen H |
CEN 15104 |
|
gross calorific value at constant volume Hov |
CEN 14918 |
|
net calorific value at constant pressure Hup |
CEN 14918 |
|
fusibility of ash, oxidising atmosphere |
Ash by 550°C |
|
shrinkage starting temperature SST |
15370-1 |
|
deformation temperature DT |
CEN 15370-1 |
|
sphere temperature ST |
|
|
hemisphere temperature HT |
CEN 15370-1 |
|
flow temperature FT |
CEN 15370-1 |
|
Fluorine F |
ISO 11724 |
|
Chlorine Cl |
CEN 15289 |
|
decomposition method |
CEN 15297 |
|
Aluminium Al |
CEN 15297 |
|
Antimony Sb |
CEN 15297 |
|
Arsenic As |
CEN 15297 |
|
Lead Pb |
CEN 15297 |
|
Cadmium Cd |
CEN 15297 |
|
Chromium Cr |
CEN 15297 |
|
Iron Fe |
CEN 15297 |
|
Cobalt Co |
CEN 15297 |
|
Copper Cu |
CEN 15297 |
|
Mangannese Mn |
CEN 15297 |
|
Nickel Ni |
CEN 15297 |
|
Quecksilber Hg |
CEN 15297 |
|
Thallium Tl |
CEN 15297 |
|
Vanadium V |
CEN 15297 |
|
Zinc Zn |
CEN 15297 |
|
Tin Sn |
CEN 15297 |
|
EOX, extractable organic halogen |
DIN 38414-S17 |
|
Ash major elements |
Ash by 550°C |
|
SiO2 |
CEN 15290 |
|
Al2O3 |
CEN 15290 |
|
Fe2O3 |
CEN 15290 |
|
CaO |
CEN 15290 |
|
MgO |
CEN 15290 |
|
Na2O |
CEN 15290 |
|
K2O |
CEN 15290 |
|
TiO2 |
CEN 15290 |
|
SO3 |
CEN 15290 |
|
P2O5 |
CEN 15290 |
|
MnO2 |
CEN 15290 |
|
BaO |
CEN 15290 |
|
SrO |
CEN 15290 |
|
particle density |
EN 15150 |
|
bulk density (analog, lower volume <5L) |
EN 15103 |
|
abrasion <3,15 mm (Ligno-Test) |
LIGNO Test |
| mecanical durability | CEN 15210 |